Pull in Ropes

The pull in ropes are tailor made according to customers´ specifications. The ropes comes with OTS protective jacket™ to protect the rope from the hard abrasion caused by the deck machinery. The qualities of the OTS pull in ropes provide safer operations, reduced operation time and lower the operational costs when compared to alternative products.

Dextron®12 Plus

Dextron®12 Plus is a torque-free, 12-strand braided rope with maximum strength-to-weight ratio and size-for-size has the same strength as steel. Dextron®12 Plus is made with Dyneema® SK78 and is an excellent wire rope replacement with extremely low stretch, superior flex fatigue and wear resistance.

Dextron®12 Plus is Type-Approved by DNV. Download certificate

Applications

Seismic Lines
Mooring lines
Winch lines
Pick-up lines
Tug assist lines
Tow lines
Fishing Lines
SPM hawsers
Subsea installation lines
Wire rope replacement
Pennants
Lifting Slings
Grommets
Messenger Lines

Special Properties

Stronger than steel wire on corresponding diameter
8 times stronger than steel with same weight
Fast and easy to splice
Floats
High abrasion resistance
Long service life
Flexible and easy to handle
High safety – low kinetic energy (low lash back)
Torque free
Dielectric and resonance properties

Characteristics:

Material	Dyneema®SK78
Colour of rope	Yellow
Elastic elongation	0,44% at 10% of breaking load 0,62% at 20% of breaking load 0,79% at 30% of breaking load
Water absorption	None
Abrasion resistance	Very good
Fatigue resistance	Excellent
UV exposure	Very good
Chemical resistance	Excellent
Melting range	144-152 ºC
Max work temp.	65ºC
Specific density	0,98 (floating)

Request techical details

Dextron® 12 Super

Maximum strength without compromise. The Dextron® 12 Super is a rope made with Dyneema® SK99 - the ultra-strong fiber. Dextron® 12 Super is the optimal choice for operations with very high demand on modulus and breaking strength.

Characteristics

Material	Dyneema® SK99
Colour of rope	Yellow with gold tracer
Elastic elongation	0,44 at 10% 0,62 at 20% 0,79 at 30% of breaking load
Water absorption	None
Abrasion resistance	Very good
Fatigue resistance	Excellent
UV exposure	Very good
Chemical resistance	Excellent
Melting range	144-152 ºC
Max work temp.	65ºC
Specific density	0,98 (floating)

Dyneema® SK99 is the latest innovation for highest level of performance. Dyneema®SK99 has the highest tenacity (42.5 cN/dtex) and modulus (1590cN/dtex) of any lightweight polymer fiber. Result: ropes that respond with micro precision resulting in maximum speed. Contact us for strength and dimensions.
Break load in accordance with DIN EN ISO 2307
Manufactured by Offshore & Trawl Supply AS – Certified according to ISO 9001:2015

Request techical details

OTS Protective jacket™: Patent no: 314459

The patented chafe gear - OTS Protective jacket™ - offers excellent protection against external abrasion and increases rope lifetime with up to five times. The "no-rupture" construction combined with the worlds most abrasion resistant synthetic fibers, makes this the best cut -and abrasion resistant cover for your ropes. The jacket is mechanically braided onto the rope for a firm and solid finish.

OTS Protective jacket™ is braided in the following combinations:

Soft eyes
Soft eyes and required length (for instance over the splices)
Exposed area on the rope
Entire rope length

OTS Protective Jacket™

Made with HMPE or polyester fiber.
The OTS Protective Jacket™ comes out as a clear winner in comparative testing of abrasion and cut resistance.
Excellent protection against wear and tear.
Patented technology

Advantages

Increases service life.
Can be braided onto entire rope or exposed areas.
Prevents rope from twisting.
Protects rope from external abrasion.
Reduced size of mooring line.
Reflective material can be woven into jacket band for better visibility.
Jacket band can be delivered in any colour.

Request techical details